Cold working
Cold working should be carried out after solution treatment. The work hardening rate of Inconel718 is greater than that of austenitic stainless steel, so the processing equipment should be adjusted accordingly, and there should be an intermediate annealing process during the cold working process.
Heat treatment
Different solution treatment and aging treatment processes will result in different material properties. Due to the low diffusion rate of γ" phase